Bàbà

Lát'ọwọ́ Wikipedia, ìwé ìmọ̀ ọ̀fẹ́
Lọ sí: atọ́ka, àwárí
Copper
29Cu
-

Cu

Ag
nickelcopperzinc
Ìhànsójú
reddish/orange metallic luster

Native copper (~4 cm in size)
Àwọn ìdámọ́ wíwọ́pọ̀
Orúkọ, àmì-ìdámọ́, nọ́mbà copper, Cu, 29
Ẹ̀ka ẹ́límẹ̀nti transition metal
Ẹgbẹ́, àsìkò, àdìpò 114, d
Ìwúwo átọ́mù 63.546(3)
Ìtòléra ẹ̀lẹ́ktrónì [Ar] 3d10 4s1
2, 8, 18, 1
Physical properties
Phase solid
Density (near r.t.) 8.94 g·cm−3
Liquid density at m.p. 8.02 g·cm−3
Melting point 1357.77 K, 1084.62 °C, 1984.32 °F
Boiling point 2835 K, 2562 °C, 4643 °F
Heat of fusion 13.26 kJ·mol−1
Heat of vaporization 300.4 kJ·mol−1
Molar heat capacity 24.440 J·mol−1·K−1
Vapor pressure
P (Pa) 1 10 100 1 k 10 k 100 k
at T (K) 1509 1661 1850 2089 2404 2834
Atomic properties
Oxidation states +1, +2, +3, +4
(mildly basic oxide)
Electronegativity 1.90 (Pauling scale)
Ionization energies
(more)
1st: 745.5 kJ·mol−1
2nd: 1957.9 kJ·mol−1
3rd: 3555 kJ·mol−1
Atomic radius 128 pm
Covalent radius 132±4 pm
Van der Waals radius 140 pm
Miscellanea
Crystal structure face-centered cubic
Copper has a face-centered cubic crystal structure
Magnetic ordering diamagnetic
Electrical resistivity (20 °C) 16.78 nΩ·m
Thermal conductivity 401 W·m−1·K−1
Thermal expansion (25 °C) 16.5 µm·m−1·K−1
Speed of sound (thin rod) (r.t.) (annealed)
3810 m·s−1
Young's modulus 110–128 GPa
Shear modulus 48 GPa
Bulk modulus 140 GPa
Poisson ratio 0.34
Mohs hardness 3.0
Vickers hardness 369 MPa
Brinell hardness 874 MPa
CAS registry number 7440-50-8
Àwọn ísótòpù dídúró jùlọ
Main article: Àwọn ísótòpù copper
iso NA half-life DM DE (MeV) DP
63Cu 69.15% 63Cu is stable with 34 neutrons
65Cu 30.85% 65Cu is stable with 36 neutrons
· r